The new generation of innovative projects has led to the use of greater amounts of reinforcement and the development of concrete with specific characteristics. It is necessary to use a material that ensures the uniformity of the cross section, as well as the adherence of the existing reinforcement, and due to this, the self-consolidating concrete becomes an technique alternative has great potential to achieve these properties. The aim of this paper is to analyze the bond behavior of self-consolidating concrete that was obtained by means of the Beam Test performed within a large experimental campaign of characterization. Four types of SCC were studied with two strength levels (40 MPa and 60MPa) and two different types of granular skeletons, using two specimens at each age (3, 7, and 28 days). All specimens were tested with a corrugated steel bar 10 mm in diameter. The results show that the adhesion tension independently of resistance presents a rapidly evolving at 7 days reached 95% of the total adhesion by 28 days.  La necesidad de proyectos innovadores ha conducido al empleo de mayores cuantías de armadura y al desarrollo de concretos con características especiales. Para ello, se hace necesario el empleo de un material que garantice la homogeneidad de la sección transversal, así como, la adherencia de la armadura existente; en este sentido, el concreto autocompactante se torna una alternativa técnica con gran potencial para atender esas propiedades. El objetivo de este trabajo es analizar los resultados de la resistencia de adherencia del concreto autocompactante obtenidos en una amplia campaña experimental. Se ha trabajado con dos niveles de resistencia a la compresión (40 y 60 MPa) y con dos esqueletos granulares distintos. Se ha empleado el ensayo de la viga (UNE 36740: 1998) para medir la tensión de adherencia a 3 edades diferentes (3, 7 y 28 días). Todas las probetas fueron ensayadas con una barra corrugada de acero de 10 mm de diámetro. Los resultados muestran que la tensión de adherencia independientemente de la resistencia, presenta una evolución rápida, alcanzando a los 7 días un 95% del total de la adherencia a los 28 días.