Influence of the bed joint thickness on the bearing capacity of the brick masonry under compression loading: an ultrasound assessment
Influencia del espesor de la junta de mortero en la capacidad de resistencia de la mampostería de ladrillo bajo cargas de compresión: una evaluación de ultrasonido.
Author
Monteagudo, Silvia M.
Casat, María Jesus
Gálvez, Jaime C.
Abstract
The aim of this paper is to analyse the influence of mortar bed joint thickness on the structural behaviour of brick-masonry specimens under compressive stress. Moreover, the progressive cracking of the material was studied during the loading process. Nine walls and nine columns were tested, combining three mortar bed joint thicknesses. Simultaneously, ultrasound, extensometer and Schmidt hammer measurements were recorded. The obtained results show that the thinner the mortar bed joint (5mm), the greater the breaking load (20.5N/mm2) and ultrasonic pulse speed. In addition, ultrasound evaluation shows good agreement with the extensometer measurements and allows accurate detection of the inner material failure. En este trabajo se analiza la influencia del espesor de la junta de mortero en la resistencia a compresión de la fábrica de ladrillo cerámico bajo esfuerzos de compresión uniaxial. Además se estudia el progresivo agrietamiento del material durante el proceso de carga. Se han ensayado nueve muros y nueve pilares, combinando tres espesores de junta de mortero realizando medidas con ultrasonidos, además se han realizado medidas con extensómetros y esclerómetro. Los resultados obtenidos muestran que a menor espesor de junta (5mm) se obtiene una mayor carga de rotura (20.5 N/mm2) y mayor valor de la velocidad de pulso ultrasónico. La medida con ultrasonidos muestra una buena correlación con las medidas extensométricas y permite una eficaz detección del agrietamiento interior del material durante el proceso de rotura.