In this study, the effects of concretes which have 250, 300, 350 and 400 kg/m3 cement in per m3 and different voltage level application (0 V, 40 V, 60 V, 80 V and 100 V AC) on concrete maturity have been investigated. It has been researched if there is relationship with maturity and compressive strength on the concrete to which stress intensity has been applied. The electrical current has been applied on fresh concretes for 24 hours whose sizes are 10 × 10 × 35 cm. Their internal temperatures of concretes have been recorded and maturity values have been calculated. It has been concluded that AC stress intensity can be used to accelerate maturity through obtaining optimum degree on concrete’s internal temperature without any compressive strength lost.En este estudio, se investigaron los efectos de los hormigones que tienen 250, 300, 350 y 400 kg/ m3 de cemento y la aplicación de diferentes niveles de voltaje (0 V, 40 V, 60 V, 80 V y 100 V AC) en la madurez del concreto. Se ha investigado si existe una relación con la madurez y la resistencia a la compresión en el concreto al que se ha aplicado la intensidad de tensión. La corriente eléctrica se ha aplicado sobre hormigones frescos durante 24 horas cuyos tamaños son 10 × 10 × 35 cm. Se han registrado las temperaturas internas de los hormigones y se han calculado los valores de madurez. Se ha llegado a la conclusión de que la intensidad de tensión de CA se puede utilizar para acelerar la madurez a través de la obtención de un grado óptimo en la temperatura interna del concreto sin pérdida de resistencia a la compresión.