The effect of increasing solid resin, and the density of manufactured Chusquea culeou Desv. particleboard, agglomerated with ureaformaldehyde was studied. The one-layer boards were 11 mm thick, and were manufactured using shaves like those used in coke layers. The Densities studied were 450, 550, 650 and 750 Kg/m3 and the resin levels 6, 7, 8, 9 and 10% based on oven-dry shave weigth. Mechanical properties were tested according to DIN standard, and were analized by linear regression. A high correlation between studied mechanical properties and density was found. The adhesive effect was significant for the bending strength only over a 600 Kg/m3 density and with a resin level over 8%. Concerning internal bond, the increase resin level is advantageous in all studied densities.Se estudia el efecto al incrementar el nivel de resina sólida como de aumentar la densidad en tableros de partículas elaboradas con virutas de Chusquea culeou Desv., aglomerados con ureaformaldehído. Los tableros se elaboraron de una sola capa, con virutas del tipo capa media, con un espesor de 11 mm. Las densidades estudiadas correspondieron a 450; 550; 650 y 750 kg/m3 ; los niveles de adhesivos estudiados fueron 6, 7, 8, 9 y 10%, basado en el peso anhidro de las virutas. Los ensayos de las propiedades mecánicas se realizaron de acuerdo con las normas DIN y se analizaron mediante regresión lineal; se encontró un alto grado de correlación entre las propiedades mecánicas estudiadas y la densidad. El efecto del adhesivo sobre la flexión fue significativo en los tableros de densidad superior a 600 kg/m3 y con niveles de adhesivo mayores a 8%. En la resistencia a la tracción, el aumento del nivel de adhesivo es positivo en todos los niveles de densidad estudiados. De acuerdo con los resultados Chusquea culeou Desv. puede ser incluida en los tableros de partículas con densidades superiores a 600 kg/m3 y con niveles de adhesivo superiores al 8%.