Mixtures of Pinus radiata D. Don back and wood particles for the production of particleboards were studied. Single layer boards with the following processing parameters were manufactured: Board thickness: 11 mm; Board density: 650 kg/m3 ; Adhesive content: 8% urea-resin solids, based on ovendry weight of particles; Bark content (%): 0; 10; 25; 40; 55; 70; 85 and 100%. A high correlation between mechanical and physical properties and board bark content was found. The observed trend shows that bark inclusion has a negative effect on mechanical properties, while the physical properties improve.Se analiza la inclusión de corteza de Pinus radiata D. Don en la elaboración de tableros de partículas, en combinación con maderas de la misma especie. Los tableros se confeccionaron de una capa, con un espesor de 11 mm y una densidad de 650 kg/m3 . Se elaboraron ocho tipos de tableros, variando el contenido de corteza desde 0 a 100% en base al peso de material leñoso en el tablero, e incluyendo los niveles 10, 25, 40, 55, 70 y 85%. Como adhesivo se empleó ureaformaldehído, en una cantidad equivalente al 8% del peso seco de las partículas. En general, se presenta una alta correlación entre las propiedades evaluadas y el nivel de corteza incorporado a los tableros. Las tendencias observadas demuestran que la inclusión de corteza de Pinus radiata D. Don tiene un efecto negativo sobre las propiedades mecánicas, pero las propiedades físicas se ven mejoradas.