Due to some basic characteristics like wood acidity and density, tepa (Laurelia philippiana Looser) is not considered suitable for particleboard production with ureaformaldehyde as adhesive. In this study the unfavourable hardening environment for ureaformaldehyde was modifyed correcting the pH-value, increasing the amount of catalyst (NH4Cl). Ammonium chloride (20% solution) was applied in six different levels: 0.5, 1.0, 1.5, 2.0, 2.5 and 3.0 percent based solid weight of resin. The pH-value and gel-time of the adhesive was reduced by increasing the amount of ammonium chloride. Increased catalyst level also significatively reduced the formaldehyde release of the boards.La madera de tepa (Laurelia philippiana Looser) presenta algunas características, como su baja densidad y su valor de pH, que resultan negativas en la fabricación de tableros de partículas con ureaformaldehído. En el presente estudio se corrigió el ambiente desfavorable para el fraguado, aumentando la cantidad de catalizador (NH4Cl). El cloruro de amonio (en solución al 20%) fue agregado en seis niveles diferentes: 0.5, 1.0, 1.5, 2.0, 2.5 y 3.0 (base resina sólida) y un testigo sin catalizador. Los resultados indican que al aumentar el nivel de catalizador se reduce el valor de pH y el tiempo de gelificación. La emanación de formaldehído también se vio significativamente disminuida al aumentar el contenido de catalizador.