Second growth Raulí (Nothofagus alpina) thinnings and Pinus radiata wood was used as raw material for the manufacturing of blockboards. As adhesive polivinyl acetate was applied. Wood yield on blockboard production and tensile strength of wood and lap joints were studied. Yield of 58% was determined for the production of blockboards with dryed N. alpina saw wood. This value was higher than those reported for P. radiata by a furniture industry (35-40%). Tensile strength of N. alpina was about 4 N, almost 40%, higher than P. radiata. There were no differences between Raulí splint and heart wood. Tensile strength of lap joints of N. alpina were superior to those required by EN 204 Standard. After air conditioning a tensile strength of about 12 N with N. alpina and 9 N with P. radiata was determined. Soaking in water for 96 hours at 20°C reduced values to 5.5 N (N. alpina) and 6.0 N (P. radiata).Se fabricaron tableros enlistonados, "blockboards", con madera proveniente del raleo de renovales de Raulí (Nothofagus alpina) y Pino Insigne (Pinus radiata) de plantaciones industriales. Como adhesivo se usó polivinil acetato. Se determinó el rendimiento y la resistencia al cizalle de la madera y de las uniones. El rendimiento de N. alpina al producir tableros desde madera aserrada seca fue de 58%, valor superior al reportado por la industria del mueble con P. radiata (35-40%). La resistencia al cizalle de la madera de Raulí fue alrededor de 4 N (40%) más alta que la de P. Insigne. No se registraron diferencias entre albura y duramen de Raulí. Las resistencias al cizalle de las uniones de Raulí superaron las exigencias de la norma EN 204. Luego de un climatizado la resistencia de N. alpina fue de 12 N, mientras que con P. radiata sólo se alcanzaron 9 N. Un tratamiento en agua a 20°C por 96 horas redujo esta propiedad a 5.5. N en N. alpina y 6.0 en P. radiata.