The present research intends to develop studies on reinforced concrete beams by applying controlled damage corrosion to cross-sectional reinforcements, thus finding relationships between different stirrups corrosion levels and shear strength due to diagonal tensile stress. Two series of eight beam specimens were constructed, each series having a stirrup spacing distance of 150 and 200 mm. The beams are exposed under wetting/drying cycles, with a 3.5% NaCl solution. In this paper, preliminary results are discussed related to the control of stirrups corrosion potential while the beams are exposed to NaCl. The obtained results will allow understanding the effect of stirrups corrosion level upon beams shear strength behavior, and the corresponding cracking patternRev. ing. constr. [online]. 2009, vol.24, n.3, pp. 259-270. ISSN 0718-5073.  http://dx.doi.org/10.4067/S0718-50732009000300004Esta investigación propone realizar estudios en vigas de concreto reforzado, en las que se induzca un deterioro controlado por corrosión en el refuerzo transversal encontrando correlaciones entre diferentes grados de corrosión en los estribos y la resistencia por cortante debido a la tensión diagonal. Se fabricaron 2 series de 8 vigas con una separación de 150 y 200 mm entre estribos para cada serie. Las vigas están siendo expuestas a ciclos de humectación utilizando una solución de 3.5% de NaCl y secado al aire libre. Aquí se discuten resultados preliminares asociados al seguimiento del potencial de corrosión de los estribos antes y durante la exposición de las vigas al cloruro de sodio. Los resultados obtenidos permitirán conocer el efecto del grado de deterioro de los estribos sobre el comportamiento por cortante en las vigas, y el correspondiente patrón de agrietamiento.Rev. ing. constr. [online]. 2009, vol.24, n.3, pp. 259-270. ISSN 0718-5073.  http://dx.doi.org/10.4067/S0718-50732009000300004