The focus of this paper is to investigate the behavior of the fresh and hardened state of alkali-activated cementitious pastes obtained from the mixture of bottom ash/BOF slag and fly ash/BOF slag. For this purpose, the properties in the fresh and hardened state were evaluated. Ten pastes were produced in two separate systems, whose proportions between ashes and BOF slag were 100:0, 75:25, 50:50, 25:75, and 0:100 (fly ash or bottom ash: BOF slag). In general, the addition of BOF steel slag works by accelerating the setting times, at room temperature curing. In addition, the stress-strain curves demonstrated that heavy ash and BOF steel slag favor the ductile behavior under axial stress. Furthermore, the addition of BOF slag can influence the properties in the fresh and hardened state. Therefore, it is feasible to use steel slag combined with coal ash in alkaline activated binary mixtures.El objetivo de este trabajo es investigar el comportamiento del estado fresco y endurecido de las pastas cementosas activadas con álcali obtenidas de la mezcla de cenizas de fondo/escoria BOF y cenizas volantes/escoria BOF. Para el propósito, se evaluaron las propiedades en el fresco y estado endurecido. Se produjeron diez pastas en dos sistemas separados, cuyas proporciones entre cenizas y escoria BOF fueron 100: 0, 75:25, 50:50, 25:75 y 0: 100 (cenizas volantes o cenizas de fondo: escoria BOF). En general, la adición de escoria de acero BOF actúa acelerando los tiempos de configuración, a temperatura ambiente de curado. Además, las curvas tensión-deformación demostraron que las cenizas pesadas y la escoria de acero BOF favorecen el comportamiento dúctil en tensión axial. Además, la adición de escoria BOF puede influir en las propiedades en estado fresco y endurecido. Por tanto, es factible utilizar escoria de acero combinada con ceniza de carbón en mezclas binarias alcalinas activadas.