This paper discusses the effects of carbonation on the microstructure of portland cement concrete for longtermdurability applications. A class C40 concrete (characteristic compression strength between 40 MPa and 44 MPaon the 28th  2  th and 91st  days, respectively.atmosphere after physical and mechanical characterization. It was observed that carbonation provoked a reduction of 5% to 12% of the concreteopen porosity accessible to water. Flexural strength values obtained after the carbonation tests revealed a decrease of12% and 25% in relation to the values obtained before tests on the 28day, according to Brazilian standard NBR 8953) was chosen for the experimental study of the carbonationeffects, from which test samples were molded for accelerated test under a 100%-CO Este trabajo analiza los efectos de la carbonatación sobre la microestructura del concreto de cementoportland para aplicaciones de durabilidad de largo plazo. Un concreto Clase C 40 (resistencia a la compresióncaracterística entre 40Mpa y 44Mpa en el día 28 de acuerdo a la norma brasileña NBR 8953) fue elegido para elestudio experimental de los efectos de la carbonatación, a cuyo objeto se moldearon muestras experimentales para unensayo acelerado bajo una atmósfera de CO2  al 100% después de la caracterización física y mecánica. Se observa que la carbonatación provocó una reducción de 5% a 12% de la porosidad abierta del concreto accesible al agua. Losvalores de resistencia a la flexión obtenidos después de las pruebas de carbonatación revelaron una disminución de12% a 25% en relación a los valores obtenidos antes de la pruebas en el día 28 y 91, respectivamente.